Type
Nickel based flux cored wire for hardfacing containing a high amount of tungsten carbides.
classification
EN ISO
14700: T Ni20
14700: T Fe20
DIN
8555: MF 21-GF-55-CGTZ
Anwendungen
This Ni-based alloy provides an excellent corrosion resistance combined with extreme abrasion resistance. OA WC2 (Ni) can be applied on all sorts of steels except on cast iron or Mn-steel. This alloy is the most wear resistant type in most hardfacing applications. In case of very fine dust abrasion It might happen that the matrix will be washed out and looses the imbedded Tungsten carbides, in this case another hardfacing product should be considdered.
Type
Nickel based flux cored wire for hardfacing containing a high amount of tungsten carbides.
Anwendungen
This Ni-based alloy provides an excellent corrosion resistance combined with extreme abrasion resistance. OA WC2 (Ni) can be applied on all sorts of steels except on cast iron or Mn-steel. This alloy is the most wear resistant type in most hardfacing applications. In case of very fine dust abrasion It might happen that the matrix will be washed out and looses the imbedded Tungsten carbides, in this case another hardfacing product should be considdered.
Eigenschaften

2400 HV nickel based corrosion resistant hardfacing alloy containing 60% tunsten carbides. OA WC2 (Ni)  has excellent flow and wetting characteristics. Multi-layer deposits are possible and worn parts can be rebuild without removing the old material. Crushed cast carbide will guaranty a long life for several wear applications. Best to be used with shielding gas M13 (Argon with 1% Oxygen) approx. 15 litres per minute.

Klassifikation
EN ISO
14700: T Ni20
14700: T Fe20
DIN
8555: MF 21-GF-55-CGTZ
Geeignet für

Rebuilding of stabilisers and other oilfield tools where maximum protection is required. Also for augers, impellers, mixer plates in the brick and clay industry and on decanter screws or hardfacing deep drilling equipment.

Schweißpositionen
PA
PB
PC
Rücktrocknung
140°C / 24 hr
Hardness / Composition
Matrix: 55HRc (± 56%)
Carbides: 2400HV (FTC ±44%)
Analyse
C Si Mn P S Ni Mo Fe Cu Al Mg Nb+V Ce W WC TFC Cr B
0.4 2.5 Rem. 44 2.7 1.7
Mechanische Gütewerte
Heat
Treatment		 RP0,2
(MPa)		 Rm
(MPa)		 A5
(%)		 Hardness
As Welded 2400 HV
Produktblatt
Konformitätserklärung