Type
Tubular SAW wire based on a 17% Chromium deposit with high Carbon content..
classification
EN ISO
14700: T Fe8
W.Nr.
1.4115
Applications

Hardfacing shafts from stainless steel parts, molt repairs, rebuilding pump parts, etc. Suitable for plating and joining equal and similar ferritic Cr-steels and cast steels. Proper weldings are subject to the recommended heat treatment. This welding wire is specially suitable for sealing surfaces on water-, steam and gas-valves, especially for sulphuric gases.

Type
Tubular SAW wire based on a 17% Chromium deposit with high Carbon content..
Applications

Hardfacing shafts from stainless steel parts, molt repairs, rebuilding pump parts, etc. Suitable for plating and joining equal and similar ferritic Cr-steels and cast steels. Proper weldings are subject to the recommended heat treatment. This welding wire is specially suitable for sealing surfaces on water-, steam and gas-valves, especially for sulphuric gases.

Properties

Higher productivity, higher deposition rates and improved wetting properties compared to solid wires with comparable analysis. Best to be used with CEWELD® FL 915 or CEWELD® FL 8111 welding flux.The deposit is resistant to seawater, thin acids and scale resistant in air and oxidizing gases up to 950°C. The weld deposit can be tempered. 

Classification
EN ISO
14700: T Fe8
W.Nr.
1.4115
Suitable for

1.4122, 1.4115 (G)X35CrMo17, 1.4313, 1.4000, 1.4001, 1.4002, Cast steels

Welding positions
PA
PB
Redrying
Not required
Analysis
C Mn Si Cr Mo
0.2 0.85 0.45 17 1
Mechanical Properties
Heat
Treatment		 RP0,2
(MPa)		 Rm
(MPa)		 A5
(%)		 Hardness
As Welded 43 HRc