Type
SP 95/5 is a Nickel-Aluminum based alloy for use as a bonding layer with the thermal spray process
classification
EN ISO
14919: 6.5
Applications
New coatings on machine parts and shafts to increase life, rebuilding wornout parts etc. Layer thickness: approximately 0.1- 0.15 mm.
Type
SP 95/5 is a Nickel-Aluminum based alloy for use as a bonding layer with the thermal spray process
Applications
New coatings on machine parts and shafts to increase life, rebuilding wornout parts etc. Layer thickness: approximately 0.1- 0.15 mm.
Propriétés

This alloy offers the highest bonding properties available for both the Flame spray process as the Arc Spray process. The wire has a high polished and clean surface to assure the best feeding and thermal spray properties. Sprayed layers of this material are-resistant to variation in high temperatures and are used as a buffer layer for all other spraying alloys. Hardness, coating macro: approximately HRc 22. Maximum working temperature: approximately 850 °C

Classification
EN ISO
14919: 6.5
Convient pour

Shafts, Clutches, Gliding surfaces, Valves, Bond coatings etc.

Positions de soudage
PC
Etuvage
Not required
Gas acc. EN ISO 14175
None
Analyse
Si Mn Cr Ti Fe B Cu Zn Sn Al Mg C S P Pb Ni Mo Nb W As
0.2 0.2 0.2 0.1 5.2 Rem.
Propriétés mécaniques
Heat
Treatment		 RP0,2
(MPa)		 Rm
(MPa)		 A5
(%)		 Hardness
As Welded 75 HB
fiche produit