Thermanit 14 K Si
Merk
Ceweld product
Type
Solid stainless steel welding wire
classification
AWS
A 5.9: ER410
EN ISO
14343-A: G Z 13
W.Nr.
1.4009
DIN
8555: MSG 5-GZ-CGTZ
Toepassingen
Overlay of carbon and low-alloy steels for resistance to corrosion, erosion, or abrasion. 410 has higher hardness and is used in valve seats to obtain better galling resistance. Normally to obtain adequate ductility, preheat and post-weld heat-treatment are required.
Type
Solid stainless steel welding wire
Toepassingen
Overlay of carbon and low-alloy steels for resistance to corrosion, erosion, or abrasion. 410 has higher hardness and is used in valve seats to obtain better galling resistance. Normally to obtain adequate ductility, preheat and post-weld heat-treatment are required.
Eigenschappen
CEWELD 410 is a martensitic stainless steel that is heat-treatable. It has a nominal weld metal composition of 12% Chromium. These weld deposits are air-hardenable that can normally be heat-treated after welding.
Classification
AWS
A 5.9: ER410
EN ISO
14343-A: G Z 13
F-nr
6
FM
5
W.Nr.
1.4009
DIN
8555: MSG 5-GZ-CGTZ
Geschikt voor
Ferritic 13 % Chrome steel,
1.4000, 1.4001, 1.4002, 1.4003, 1.4006, 1.4008, 1.4021, 1.4024,
X6Cr13, X6CrAl13, X10Cr13, X15Cr13, X20Cr13, G-X10Cr13
AISI 410, 420
Goedkeuringen
CE
Lasposities
Gas acc. EN ISO 14175
M20, M21, M11, C1
Mechanische waarden
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
|---|---|---|---|---|
| As Welded | 400 | 600 | 22 | 35 HRc |